Drying-rewetting cycles in ordinary Portland cement mortars investigated by electrical impedance spectroscopy

Abstract

Changes caused in the porous microstructure of ordinary Portland cement (OPC) mortars were studied using electrical impedance spectroscopy (EIS) and equivalent circuit (EqC). Two successive processes, at 20 °C and 50 °C, consisting of several drying-rewetting cycles, were applied to the mortars. After each cycle, the electrical impedance and the amount of water absorbed were measured. The EIS-EqC methodology allowed to find two distributed impedance relaxations, associated to capillary and gel-C-S-H porosities, respectively. At room temperature any microstructural change was not detected. Nevertheless, at 50 °C two microstructural changes were inferred: 1) the volume of accessible porosity increased (pore coarsening) and 2) the surface of the conductive path through C-S-H gel became more conductive (surface smoothing).