Total oxidation of naphthalene at low temperatures using palladium nanoparticles supported on inorganic oxide-coated cordierite honeycomb monoliths

Por favor, use este identificador para citar o enlazar este ítem: http://hdl.handle.net/10045/40176
Información del item - Informació de l'item - Item information
Título: Total oxidation of naphthalene at low temperatures using palladium nanoparticles supported on inorganic oxide-coated cordierite honeycomb monoliths
Autor/es: Varela Gandía, Francisco José | Berenguer-Murcia, Ángel | Lozano Castelló, Dolores | Cazorla-Amorós, Diego | Sellick, David R. | Taylor, Stuart H.
Grupo/s de investigación o GITE: Materiales Carbonosos y Medio Ambiente
Centro, Departamento o Servicio: Universidad de Alicante. Departamento de Química Inorgánica | Universidad de Alicante. Instituto Universitario de Materiales
Palabras clave: Oxidation | Naphthalene | Palladium nanoparticles | Cordierite honeycomb monoliths
Área/s de conocimiento: Química Inorgánica
Fecha de publicación: 4-jul-2013
Editor: Royal Society of Chemistry
Cita bibliográfica: Catalysis Science & Technology. 2013, 3: 2708-2716. doi:10.1039/C3CY00323J
Resumen: A study on the preparation of thin films of ZSM-5 and BETA zeolites, and a SAPO-5 silicoaluminophosphate, supported on cordierite honeycomb monoliths by in situ synthesis was carried out for their use as catalyst supports. Furthermore γ-Al2O3 was also coated onto a cordierite honeycomb monolith by a dip-coating method for use as a standard support. Structured monolithic catalysts were prepared by impregnation of the aforementioned coated monoliths with polymer-protected Pd nanoparticles. The monolithic catalysts have been tested for the total oxidation of naphthalene (100 ppm, GHSV 1220 h−1). From the combined use of the zeolite with polymer-protected nanoparticles, enhanced catalytic properties have been found for the total abatement of naphthalene. The Pd/MBETA and Pd/MZSM-5 catalytic monoliths have shown excellent activity with a high degree of stability, even after undergoing accelerated ageing experiments.
Patrocinador/es: The authors would like to thank the Spanish MINECO, Generalitat Valenciana, and FEDER (Projects CTQ2012-31762 and PROMETEO/2009/047) for financial support. F. J. Varela-Gandía thanks the University of Alicante for a PhD studentship. Á. Berenguer-Murcia thanks the Spanish Ministry for Economy and Competitiveness for a Ramón y Cajal fellowship (RyC 2009-03913).
URI: http://hdl.handle.net/10045/40176
ISSN: 2044-4753 (Print) | 2044-4761 (Online)
DOI: 10.1039/C3CY00323J
Idioma: eng
Tipo: info:eu-repo/semantics/article
Derechos: © The Royal Society of Chemistry
Revisión científica: si
Versión del editor: http://dx.doi.org/10.1039/C3CY00323J
Aparece en las colecciones:INV - MCMA - Artículos de Revistas

Archivos en este ítem:
Archivos en este ítem:
Archivo Descripción TamañoFormato 
Thumbnail2013_Varela_etal_CS&T_final.pdfVersión final (acceso restringido)2,44 MBAdobe PDFAbrir    Solicitar una copia
Thumbnail2013_Varela_etal_CS&T.pdfVersión revisada (acceso abierto)940,87 kBAdobe PDFAbrir Vista previa


Todos los documentos en RUA están protegidos por derechos de autor. Algunos derechos reservados.