Characterisation of montmorillonites simultaneously modified with an organic dye and an ammonium salt at different dye/salt ratios. Properties of these modified montmorillonites EVA nanocomposites

Por favor, use este identificador para citar o enlazar este ítem: http://hdl.handle.net/10045/46372
Información del item - Informació de l'item - Item information
Título: Characterisation of montmorillonites simultaneously modified with an organic dye and an ammonium salt at different dye/salt ratios. Properties of these modified montmorillonites EVA nanocomposites
Autor/es: Beltrán, M.I. | Benavente Domenech, Verónica | Marchante Rodríguez, Verónica | Dema, H. | Marcilla, Antonio
Grupo/s de investigación o GITE: Procesado y Pirólisis de Polímeros | Residuos, Energía, Medio Ambiente y Nanotecnología (REMAN)
Centro, Departamento o Servicio: Universidad de Alicante. Departamento de Ingeniería Química | Universidad de Alicante. Instituto Universitario de Ingeniería de los Procesos Químicos
Palabras clave: OMt EVA nanocomposites | CPN | Modified montmorillonite characterisation | Dye | Nanopigment
Área/s de conocimiento: Ingeniería Química
Fecha de publicación: ago-2014
Editor: Elsevier
Cita bibliográfica: Applied Clay Science. 2014, 97-98: 43-52. doi:10.1016/j.clay.2014.06.001
Resumen: In this work, a sodium montmorillonite (Na+-Mt) was modified with two molecules simultaneously, an organic dye, methylene blue (MB), and ethyl hexadecyl dimethyl ammonium (EHDDMA). The synthesised organo-montmorillonites (OMt) combining different proportions of the two molecules were thoroughly characterised and mixed with ethylene vinyl acetate copolymer (EVA) in order to check the ability of these OMt as pigments and reinforcing additives. The synthesised OMt combining both surfactants, MB and EHDDMA, present higher interlayer distances than those with only MB, which were employed in previous works as nanopigments. When these OMt were incorporated in the EVA matrix, the obtained clay polymer nanocomposites (CPN) showed a high exfoliation degree of the OMt in the polymer, in such a way that at 80% of the cationic exchange capacity (CEC) of the Mt exchanged with EHDDMA, most of the OMt was exfoliated. Moreover, all the obtained CPN showed an increase in the Young's Moduli compared to the EVA reference, and especially those containing higher amounts of MB. The thermal stability of the CPN also increases with the MB content, compared to other CPN including conventional surfactants. The hiding power and colouring power achieved in the CPN are higher even with a much lower load of MB when EHDDMA is exchanged in the Mt.
Patrocinador/es: The authors wish to thank the “Vicerrectorado de Investigación, Desarrollo e Innovación” of the University of Alicante for the research initiation grant (BII5414).
URI: http://hdl.handle.net/10045/46372
ISSN: 0169-1317 (Print) | 1872-9053 (Online)
DOI: 10.1016/j.clay.2014.06.001
Idioma: eng
Tipo: info:eu-repo/semantics/article
Derechos: © 2014 Elsevier B.V.
Revisión científica: si
Versión del editor: http://dx.doi.org/10.1016/j.clay.2014.06.001
Aparece en las colecciones:INV - GTP3 - Artículos de Investigación sobre Procesado de Polímeros

Archivos en este ítem:
Archivos en este ítem:
Archivo Descripción TamañoFormato 
Thumbnail2014_Beltran_etal_ApplClayScience_final.pdfVersión final (acceso restringido)2,36 MBAdobe PDFAbrir    Solicitar una copia


Todos los documentos en RUA están protegidos por derechos de autor. Algunos derechos reservados.