Fire-resistance, physical, and mechanical characterization of particleboard containing Oceanic Posidonia waste

Abstract

In this work, particleboards manufactured with Oceanic Posidonia waste and bonded with cement are investigated. The particleboards are made with 3/1.5/0.5 parts of cement per part of Posidonia waste. The physical properties of bulk density, swelling, surface absorption, and dimensional changes due to relative humidity as well as the mechanical properties of modulus of elasticity, bending strength, surface soundness, perpendicular tensile strength and impact resistance are studied. In terms of the above properties, the best results were obtained for particleboards with high cement content and when the waste “leaves” are treated (crushed) before board fabrication, due to internal changes to the board structure under these conditions. Based on the results of fire tests, the particleboard is non-flammable without any fire-resistant treatment.

En esta investigación se han diseñado y fabricado tableros con residuo de Posidonia Oceánica y cemento. Los tableros se han fabricado con 3/1.5/0.5 partes de cemento por cada parte de Posidonia estudiándose sus propiedades físicas (densidad, hinchazón, absorción superficial, variaciones dimensionales por humedad) y mecánicas (módulo de elasticidad, resistencia a flexión, al arranque de superficie, al arranque de tornillo, a la tracción perpendicular y al choque). Se observa una mejora de los resultados de resistencia mecánica con el incremento de la cantidad de cemento y si la hoja del residuo es previamente tratada ya que proporciona una mejor estructura interna en el tablero. Además, tras los ensayos de reacción al fuego, se observa que el material es no inflamable sin ningún tipo de tratamiento ignifugante.